Lazè soude sou alyaj aliminyòm
Alyaj aliminyòm gen avantaj ki genyen nan dansite ki ba, gwo fòs ak bon rezistans korozyon, kidonk yo lajman ki itilize nan endistri otomobil, nouvo enèji, ayewospasyal ak endistri konstriksyon. Kounye a, yo te lajman itilize soude lazè nan pwodiksyon an nan pwodwi alyaj aliminyòm. Konpare ak metòd tradisyonèl soude, soude lazè ka bay pi wo efikasite pwodiksyon, pi bon kalite soude, ak reyalize soude ak presizyon wo ak automatisation nan estrikti konplèks.
Lazè soude se yon teknoloji nan ki yon lazè gwo entansite gaye sou sifas metal la, epi metal la fonn ak Lè sa a, refwadi ak kristalize yo fòme yon soude nan kouti a tèmik ant lazè a ak metal la. Dapre mekanis nan aksyon tèmik nan soude lazè, li ka divize an de kalite: soude kondiksyon tèmik ak soude pénétration gwo twou san fon. Se soude kondiksyon tèmik sitou itilize pou anbalaj soude oswa mikwo-nano soude nan pati presizyon; lazè gwo twou san fon pénétration soude se sitou itilize pou materyèl soude ki mande pou pénétration konplè. Pami yo, pwosesis la soude pral vaporize materyèl la, ak fenomèn nan keyhole ap parèt nan pisin lan fonn. Li se metòd ki pi lajman itilize lazè soude kounye a, epi li se tou metòd la pi pito pou soude alyaj aliminyòm. Materyèl oksilyè, ekipman soude senp, pa gen okenn consommables, fasil otomatize. 02 Dezavantaj: Kondisyon yo pou fim nan soude yo wo, kidonk soude a fasil koule; pwen depa ak pwen final soude a fasil pou pwodwi pwen kle yo; estabilite nan pwosesis la soude se jeneral, ak domaj soude yo fasil rive. 03Ka: Bati dekorasyon endistri - 5 seri aliminyòm alyaj pòt ankadreman soude.
Akòz pwopriyete fizik nannan alyaj aliminyòm, tankou absòpsyon lazè ki ba, pwen bouyi ki ba nan eleman alyaj, segondè konduktiviti tèmik, segondè koyefisyan ekspansyon tèmik, ranje tanperati solidifikasyon relativman lajè, kontraksyon solidifikasyon segondè, viskozite ki ba ak absòpsyon idwojèn segondè nan likid. eta, elatriye, se konsa domaj tankou porositë ak fant cho yo fasil pwodwi pandan pwosesis la soude lazè. Pami yo, porosite se fòm ki gen plis chans nan defo nan pwosesis la nan soude lazè alyaj aliminyòm. Li pral detwi konpak nan metal la soude, febli zòn nan transvèsal efikas nan soude a, epi redwi pwopriyete yo mekanik ak rezistans korozyon nan soude a. Se poutèt sa, mezi efikas yo dwe pran. Mezi pou anpeche jenerasyon porositë ak amelyore kalite entèn soude a.
Laser fusion welding porosity suppression method 01 Suppresses welding porosity through pre-welding surface treatment. Pre-welding surface treatment is an effective method to control metallurgical porosity in aluminum alloy laser welds. Usually, the surface treatment methods include physical and mechanical cleaning and chemical cleaning. After comparison, the process of chemically treating the surface of the test plate (metal cleaning agent cleaning - water washing - alkali cleaning - water washing - acid washing - water washing - drying) is the best. Among them, 25NaH (sodium hydroxide) solution is used for alkaline cleaning to remove the surface thickness of the material, and 20% HN03 (nitric acid) + 2% (hydrogen fluoride) aqueous solution is used for pickling to neutralize the residual alkali solution. After the surface treatment of the test plate, the welding is carried out within 24 hours , When the test plate stays for a long time after treatment, wipe it with anhydrous alcohol before welding. 02 Suppressing welding porosity through welding process parameters The formation of weld porosity is not only related to the quality of the surface treatment of the weldment, but also related to the welding process parameters. The influence of welding parameters on the weld porosity is mainly reflected in the penetration of the weld, that is, the back The effect of aspect ratio on stomata. It can be seen from the test that when the back-to-width ratio of the weld is R>0.6, distribisyon an konsantre nan porositë chèn nan soude a ka efektivman amelyore. Se rezidi nan porositë nan soude a elimine.
03 Atravè seleksyon kòrèk gaz pwoteksyon ak pousantaj koule pou siprime porositë soude Seleksyon gaz pwoteksyon dirèkteman afekte bon jan kalite, efikasite ak pri soude. Pandan pwosesis la soude lazè, piki ki kòrèk la nan gaz pwoteksyon ka efektivman diminye porositë soude. Ar (agon) ak He (elyòm) yo itilize pou pwoteje sifas soude a. Nan pwosesis la nan alyaj aliminyòm soude lazè, degre nan ionizasyon nan Ar ak Li nan lazè a se diferan, sa ki lakòz fòmasyon soude diferan. Rezilta a montre ke chwa a nan Ar Porosite an jeneral nan soude a jwenn kòm gaz la pwoteksyon se mwens pase sa yo ki nan soude a lè yo chwazi Li kòm gaz la pwoteksyon. An menm tan an, nou ta dwe tou peye atansyon sou lefèt ke yon gwo kantite plasma ki te pwodwi pa soude pa ka soufle ale si to koule gaz la twò piti (10L / min), sa ki fè pisin lan soude enstab ak ogmante pwobabilite a. nan fòmasyon porosite. Pousantaj gaz la modere (apeprè 15L / min) epi yo ka jwenn plasma a. Kontwòl efikas, gaz pwoteksyon an gen yon bon efè anti-oksidasyon sou pisin nan fonn, ak porosite a se minim. Twòp koule lè akonpaye pa presyon gaz twòp, se konsa ke yon pati nan gaz pwoteksyon an melanje nan pisin lan fonn, ak porosite a ogmante.
Suppression de porosité défauts nan lazè soudi alyaj aliminyòm te toujou yon pwoblèm nan endistri a. Ki afekte nan pèfòmans nan materyèl la alyaj aliminyòm tèt li, fenomèn nan pa gen okenn porosite nan soude pa ka konplètman evite pandan pwosesis la soude, men porosite a ka sèlman redwi. Atravè optimize pwosesis la anvan ak apre soude, nou te rezime ak pwopoze twa fason yo siprime porosite atravè eksperyans pou referans pa kòlèg nan endistri an. DOTSLASER lazè pa sèlman konsantre sou rechèch ak inovasyon nan teknoloji pwodwi lazè, men tou, devlope ak eksplore divès kalite teknoloji pwosesis lazè, epi li gade pou pi devan pou diskite ak plis ekspè endistri ankouraje amelyorasyon nan teknoloji pwosesis lazè nan peyi mwen an.